A method comprises providing a molten aluminum alloy selected from the group consisting of 6000 series aluminum alloys comprises chromium (Cr) in a range of between 0.001 wt % to 0.05 wt %. The molten aluminum alloy is formed into a formed body having beta-AlFeSi particles. The formed body is solution heat treated at a temperature in a range of 1,025-1,050° F. to form a heat-treated body. The solution heat treating transforms substantially all of the beta-AlFeSi particles into alpha-AlFeSi particles such that the heat-treated body is substantially free of the beta-AlFeSi particles.